PRODUCT NAME :
bearing steel
STANDARD:
GB/T18254-2002 ISO683-17
GRADE COMPARISION:
|
GB |
ГОСТ |
ASTM |
BS |
JIS |
NF |
DIN |
|
GCr9 |
ШX9 |
E51100 |
|
SUJ1 |
100C5 |
105Cr4 |
ULTRASONIC STANDARD:
GB/T6402-2008 / SEP921-84. ASTM A388
CHEMICAL COMPOSITION:
|
C |
Si |
Mn |
P≤ |
S≤ |
Cr |
|
1.0/1.10 |
0.15/0.35 |
0.25/0.45 |
0.025 |
0.025 |
0.90/1.20 |
HEAT TREATMENT SPECIFICATION:
Common anneaing :790-810℃，furnace cooling to 650℃ HB170-207
Spheroidizing （HBW) :179-207
MECHANICAL PROPERTIES:
Hardness (HRC):25.8
Tensile strength (MPa):861.3
Yield strength (MPa):518.42
Elongation :(%):27.95 D
ELIVERY CONDITION : annealed
DIMENSION : mm
|
ROUND STEEL BAR |
COIL ROD |
WIRE |
SQUARE/ FLAT |
|
FORGED BAR |
ROLLED BAR |
HOT ROLLED |
COLD DRAW |
FORGED |
ROLLED |
|
100-700 |
16-250 |
∮5.5-20 |
∮0.2-13 |
120-800×120-800 |
5-38×44-150 10-90×60-305 |
APPLIED RANGE:
Bearing steel is the general term for alloy steel used in the manufacture of bearing races and moving parts of all types of roller
bearings. High carbon and chromium bearing steel is widely applied in the manufacture of pin rollers and sleeves on driving shaft
used in auto components, construction machinery, combustion engines, electric locomotive, machine tools, tractors, steel rolling
equipment, and drilling and exploration equipment for mining industry. Carburized bearing steel is mainly used in railway locomotives
and wind turbines. The high-grade bearing steel products developed with proprietary technology have been highly appraised by six
leading bearing manufacturers in the world.
REMARK：
Above listed parameters and sepcification only for reference . Specific parameters according to standard. Requirments beyond standard
will be negotiate by both sides .
Delivery state:annealed, spheroidal annealed, quenched & tempered ,bright bar, cold-drawn, etc.
Listed specifications are only typical grades; products of required specifications can be developed/produced per international, Chinese
or industry standards, or based on agreements with customers.